Blown Linear Low Density (LLDPE) Film

Conversion Calculator

Typical Film Properties of BFI 6407.67 LLDPE

BFI 6407.67 LLDPE is a narrow molecular weight Hexene Copolymer designed for applications that require outstanding environmental stress crack resistance. This resin offers good processability with minimal warpage and outstanding toughness for cold temperature durability.

Properties	Units	ASTM Method	Typical Values
Resin Properties:
Melt Index	g/10 min	D 1238	6.8
Density	g/cm³	D 1505	0.936
Following properties are based on Compression molded samples; no film specifications are available.
Tensile Strength @ Yield	psi	D 638 Type IV 50 mm/min	2500
Thermal
Vicant Softening Temperature	º F	D 1525	234
Peak Melting Temperature	º F	D 3418	261
Flexural Modulus
1 % Secant Modulus	psi	D 790B	110,000
2 % Secant Modulus	psi	D 790B	93,000
Environmental Stress-Crack Resistance
10% lgepal, F50	hr	D 1693B	240

^{NOTE: Data developed under Laboratory conditions and are not to be used as specification, maxima or minima. ASTM procedures (where applicable) were used for these tests. The data are intended as a general guide only and do not necessarily represent results that may be obtained elsewhere. The use of these products must be guided by the user's own methods of selection of proper formulation. BFI disclaims any responsibility for misuse or misapplication of its products. BFI MAKES NO WARRANTY OF MERCHANTABILITY AND THERE IS NO WARRANTY THAT GOODS SUPPLIED SHALL BE FIT FOR ANY PARTICULAR PURPOSE. BFI's liability and customer's exclusive remedy for any claims arising out of sales of its products are expressly limited at customer option to replacement of nonconforming goods only.}